RESUMO
Objective: Fabrication and optical characterization of close-packed 225 nm SiO2 -based colloidal crystals. Materials and methods: The vertical convective self-assembly method is used to grow high-quality 225 nm close-packed SiO2-based colloidal crystals. An annealing process (550°C) is made in order to improve the mechanical stability of the sample. Optical characterization is done by angle-resolved transmission spectroscopy (A-RTS) and structural characterization by Scanning Electron Microscopy (SEM). Results: Both, A-RTS and SEM, show that with the vertical convective self-assembly method, with the appropriate parameters of temperature of evaporation (60°C), volume fraction of the colloidal suspension (0.2% w/w) and acidity (pH=6), highly ordered close packed face centered cubic (fcc) SiO2 based colloidal crystals are obtained. Conclusions: The growth of high-quality (long range order and defect-free) face centered cubic opalbased photonic crystals is reported.
Objetivo: Fabricación y caracterización óptica de cristales coloidales de esferas de SiO2 de 225 nm de diámetro y empaquetamiento fcc. Materiales y métodos: Se producen cristales coloidales de 225 nm de diámetro de alta calidad mediante la técnica convectiva de auto-ensamblado de deposición vertical. Se hace, adicionalmente, un proceso de recocido (550°C) con el fin de mejorar la estabilidad mecánica de la estructura. La caracterización óptica se lleva a cabo por espectroscopia de transmisión resuelta en ángulo (A-RTS) y la caracterización estructural mediante microscopía electrónica de barrido (SEM). Resultados: Ambos, A-RTS y MEB, muestran que con el método utilizado y con los parámetros adecuados de temperatura de evaporación (60°C), fracción en volumen de la suspensión coloidal (0,2% w / w) y acidez (pH = 6) se obtienen cristales coloidales de SiO2 con empaquetamiento compacto fcc altamente ordenados. Conclusiones: Se reporta el crecimiento de ópalos artificiales con empaquetamiento compacto fcc altamente ordenados (libre de defectos y con ordenamiento a largo alcance).
Objetivo: Fabricação e caracterização óptica de cristais coloidais de esferas de SiO2 de 225 nm de diâmetro e embalagem fcc. Materiais e métodos: Foram produzidos cristais coloidais de 225 nm de diâmetro de alta qualidade através da técnica convectiva de automontagem de deposição vertical. Faz-se, adicionalmente, um processo de recozimento (550°C), a fim de melhorar a estabilidade mecânica da estrutura. A caracterização óptica foi realizada por espectroscopia de transmissão em ângulo (A-RTS) e a caracterização estrutural utilizando microscopia eletrônica de varredura (MEV). Resultados: Ambos, A-RTS e MEV mostram que com o método utilizado e com os parâmetros adequados de temperatura de evaporação (60°C), fração de volume da suspensão coloidal (0,2% w / w) e acidez (pH = 6) são obtidos cristais coloidais de SiO2 com embalagem compacto fcc altamente ordenados. Conclusões: Registrou-se o crescimento de opalas artificiais com embalagem compacto fcc altamente ordenadas (livres de defeitos e de ordem de longo alcance).
RESUMO
Polymer-based organic light-emitting diodes (OLEDs) with the structure ITO / PEDOT:PSS / MDMO-PPV / Metal were prepared by spin coating. It is known that electroluminescence of these devices is strongly dependent on the material used as cathode and on the deposition parameters of the polymer electroluminescent layer MDMO-PPV. Objective. In this work the effect of i) the frequency of the spin coater (1000-8000 rpm), ii) the concentration of the MDMO-PPV: Toluene solution, and iii) the material used as cathode (Aluminium or Silver) on the electrical response of the devices, was evaluated through current-voltage (I-V) measurements. Materials and methods. PEDOT:PPS and MDMO-PPV organic layers were deposited by spin coating on ITO substrates, and the OLED structure was completed with cathodes of aluminium and silver. The electric response of the devices was evaluated based on the I-V characteristics. Results. Diodes prepared with thinner organic films allow higher currents at lower voltages; this can be achieved either by increasing the frequency of the spin coater or by using concentrations of MDMO-PPV: Toluene lower than 2% weight. A fit of the experimental data showed that the diodes have two contributions to the current. The first one is attributed to parasitic currents between anode and cathode, and the other one is a parallel current through the organic layer, in which the carrier injection mechanism is mediated by thermionic emission. Conclusions. The results of the fitting and the energy level alignment through the whole structure show that PPV-based OLEDs are unipolar devices, with current mainly attributed to hole transport.
Se fabricaron diodos orgánicos emisores de luz (OLEDs) con la estructura ITO / PEDOT:PSS / MDMO-PPV / Metal mediante la técnica de spin coating. Es ampliamente conocido que la electroluminiscencia de estos diodos depende fuertemente del material usado como cátodo y también de los parámetros de crecimiento de la capa del polímero electroluminiscente MDMO-PPV. Objetivo. En este trabajo el efecto de i) la frecuencia del spin coater (1000-8000 rpm), ii) la concentración de la solución MDMO-PPV: Tolueno y iii) el material usado como cátodo (plata o aluminio) sobre la repuesta eléctrica de los dispositivos, fue evaluado a través de medidas de corriente-voltaje (I-V). Materiales y métodos. Películas delgadas de los materiales orgánicos PEDOT:PSS y MDMO-PPV fueron depositados por spin coating sobre sustratos de ITO, y la estructura del OLED fue terminada con cátodo de plata y aluminio. La respuesta eléctrica de los dispositivos fue evaluada a través de su característica I-V. Resultados. Los diodos fabricados con películas orgánicas más delgadas son los que suministran mayores corrientes a menores voltajes. Esto puede lograrse ya sea incrementando la frecuencia de rotación del spin coating o usando concentraciones de MDMO-PPV: Tolueno menores al 2% en peso. Un ajuste de los datos experimentales demostró que los diodos poseen contribuciones de una corriente parásita entre ánodo y cátodo, y otra corriente paralela en donde el mecanismo predominante de inyección de portadores a la capa orgánica es a través de emisión termoiónica. Conclusiones. El ajuste de los datos experimentales, junto con la posición de niveles de energía a través de la heteroestructura, demuestra que los OLEDs basados en derivados de PPV son dispositivos unipolares, en el que la corriente se atribuye principalmente a transporte de huecos.
Foram fabricados diodos orgânicos emissores de luz (OLEDs) com a estrutura de ITO / PEDOT: PSS / MDMO-PPV / metal, pela técnica de spin coating. É amplamente conhecido que a eletroluminescência destes diodos depende fortemente do material utilizado como cátodo, e também dos parâmetros de crescimento da camada de polímero eletroluminescente MDMO-PPV. Objetivo. Neste trabalho o efeito de i) a freqüência do spin coater (1000-8000 rpm), ii) a concentração da solução MDMO-PPV: Tolueno e iii) o material utilizado como cátodo (prata ou alumínio) sobre a resposta elétrica dos dispositivos, foi avaliado por medidas de corrente-voltagem (I-V). Materiais e métodos. Películas finas de materiais orgânicos PEDOT: PSS e MDMO-PPV foram depositadas por spin coating sobre substratos de ITO e a estrutura do OLED foi terminada com cátodo de prata e de alumínio. A resposta elétrica dos dispositivos foi avaliada pela sua característica I-V. Resultados. Os diodos feitos de películas orgânicas finas fornecem maiores correntes a menores voltagens. Isto pode ser conseguido, quer através do aumento da velocidade de rotação do spin coating ou usando concentrações de MDMO-PPV: Tolueno menores de 2% em peso. Um ajuste dos dados experimentais mostrou que os diodos têm uma contribuição de uma corrente parasita entre anodo e catodo, e outra corrente paralela, onde o principal mecanismo da injeção de portadores da camada orgânica é através da emissão termiônica. Conclusões. O ajuste dos dados experimentais, juntamente com a posição dos níveis de energia através da heteroestrutura, mostra que os OLEDs baseados em derivados de PPV são dispositivos unipolares, onde a corrente é atribuída principalmente ao transporte de ocos.
